Audited Supplier
MC-PU90
Synthetic Rubber
Polyurethane Rubber
Light Yellow Liquid
Liquid Rubber
Liquid Polyurethane Rubber
Molding and Casting
Clear Yellow
90 Shore a
2500 Cps
1:1
6~9 Mins
24 Hours
18~25MPa
70~85n/mm
400~500%
6~8 Months
MC SILICONE
20kg/Drum or 200kg/Drum
REACH, MSDS, SGS
Dongguan, China
390950000
Product Description
90 Shore A Liquid Polyurethane Rubber for Casting PU Roller/PU Wheel
Product Description
Liquid polyurethane rubber consists of A&B component, B is curing agent, and A is polyurethane prepolymer. Liquid polyurethane rubber can also be used as a concrete or cement stamping mold as well as for making hard durable rubber parts for machinery or automotive applications.
Characteristics:
Liquid polyurethane rubber has excellent processing properties, solid in common temperature, shorter gel time, and regulating color by adding pigment. The ware has good properties of abrasive resistance, hydrolysis resistance, transparent, good resilience, stable dimension.
Application:
Substitute for Silicon rubber to make the mould of "cultural stone". Liquid polyurethane rubber also applies to electrical equipment potting, rubber rollers, Ski and snowboard ,rubber plates, rubber wheels, shoe models and others.
| A | Type | MCPU40 A | MCPU50 A | MCPU60 A | MCPU70 A | MCPU80 A | MCPU90 A |
| Appearance | Colorless or light yellow transparent liquid | ||||||
| Viscosity(30ºC)mPa·s/ | 2500±300 | ||||||
| B | Type | MCPU40 B | MCPU50 B | MCPU60 B | MCPU70 B | MCPU80 B | MCPU90 B |
| Appearance | Light yellow liquid | ||||||
| Viscosity(30ºC)/mPa·s | 560±200 | ||||||
| Ratio A:B(mass ratio) | 1:1 | ||||||
| Appearance | Light yellow | ||||||
| Operation temperature/ºC | 25~40 | ||||||
| Gel time(30ºC)*/min (variable) | 25-30 | 25-30 | 25-35 | 20-30 | 8-14 | 6-9 | |
| Hardness (shore A) | 40±3 | 50±3 | 60±3 | 70±3 | 80±3 | 90±3 | |
| Tensile strength/MPa | 4-7 | 5-8 | 5-8 | 8-11 | 9-14 | 18-25 | |
| Elongation at break/ % | 500-600 | 400-500 | 300-400 | 250-350 | 350-550 | 400-500 | |
| Tear strength/(kN/m) | 18-22 | 18-22 | 20-25 | 26-30 | 50-60 | 70-85 | |
| Rebound/ % | 30-35 | 30-35 | 30-35 | 30-35 | 36-40 | 32-35 | |
| Specific gravity(25ºC)(g/ cm3) | 1.18 | ||||||
USING INSTRUCTION
1.Liquid urethanes are moisture sensitive and will absorb atmospheric moisture. Mixing tools and containers should be clean and made of metal or plastic.
2. Stir Part B thoroughly before dispensing. After dispensing equal amounts of Parts A and B into mixing container, mix thoroughly for about 3 minutes making sure that you scrape the sides and bottom of the mixing container several times.
If mixing large quantities at one time, use a mechanical mixer for 3 minutes followed by careful hand mixing for one minute as directed above. Then, pour entire quantity into a new, clean mixing container and do it all over again.
3. Vacuum de-airing equipment is recommened if available.Vacuum degassing prior to pouring mixture will further reduce entrapped air.
4. For best results, pour your mixture in a single spot at the lowest point of the containment field.
5. A small-scale test is recommended before mass production.
6. For better performance, allow the mixture dry for 24 hours before demolding. It can also be heated for post curing.
7.Release agent should be applied to the mold before each casting.
8.Materials should be stored and used in a warm environment (73°F/23°C).
Storage:Store in cool and dry place. If you can't use one drum up at a time, please inject N2.The storage time of original packing is 6 months.
1.Re-cap the bottles immediately after use.
2.Extend-It aerosol nitrogen blanket can be used to protect the product from moisture contamination.
Package:20Kg/ steel drum;200kg/drum
Sample Package: 500g A+500g B