PRODUCT NAME: 70 ºC PVC Environmental Friendly Insulation Material
PRODUCT CODE: T-PV004-J-70
General Description
Base on PVC resin, this product is PVC insulation material made by mixing, plasticizing, and granulating with plasticizers, stabilizers, and other additives. PVC plastic has good dielectric properties and is widely used in the insulation layer of wires and cables, as well as in the manufacture of electrical equipment.
Feature
Good insulation;
PVC plastic has weather resistance;
Chemical corrosion resistance;
Plasticity and flexibility;
Application
Instrument communication cables, insulation layer for cables 600/1000V and below, in accordance with PVC/C in GB5023 and J-70 in GBT/8815-2008;
Widely used in pvc pipes, window profiles, films, sheets, tubes, shoes, fittings;
Appearance
70 ºC PVC insulation material should be made into uniformly sized particles with a particle size of 4mm × 4mm × 3mm, or ф 4× (2-4) mm. Good plasticization, uniform color, and no obvious impurities.
Color
The color is determined through negotiation between the supply and demand parties.
Technical Analysis
Processing
Using a general extruder for processing, L/D≥20
Adjust appropriately according to the equipment and extrusion status.
The following temperature profile of extruder is recommended:
Storage and transport
It should be packaged in moisture-proof packaging, with polyethylene film bags for the inner bag and kraft paper composite bags for the outer bag, with a net weight of (25.0 ± 0.2) kg per bag. Other packaging methods agreed upon by both the seller and the purchaser are allowed.
During the transportation of the product, it should not be damaged by abnormal conditions such as sun, rain, and immersion in water. It should be kept clean, dry, not contaminated, and the packaging should be kept intact.
The product should be stored in a clean, cool, dry, and ventilated warehouse, and the storage period should not exceed six months from the date of production.
What We Have In The Field Of Telecom Optical & Electric Cable :
1>Mature and Efficient Supply Chain System And Rich Industrial Resources
2>Complete Materials Demand Solutions For Cable Manufacturing And Technical Services
3>Overall Solutions And Customized Services In Factory Design, Equipment Configuration, Product Development And Rawmaterial Supply
*Quotation Varies According To Customer's Requirements And Quantity Of Produ
PRODUCT CODE: T-PV004-J-70
General Description
Base on PVC resin, this product is PVC insulation material made by mixing, plasticizing, and granulating with plasticizers, stabilizers, and other additives. PVC plastic has good dielectric properties and is widely used in the insulation layer of wires and cables, as well as in the manufacture of electrical equipment.
Feature
Good insulation;
PVC plastic has weather resistance;
Chemical corrosion resistance;
Plasticity and flexibility;
Application
Instrument communication cables, insulation layer for cables 600/1000V and below, in accordance with PVC/C in GB5023 and J-70 in GBT/8815-2008;
Widely used in pvc pipes, window profiles, films, sheets, tubes, shoes, fittings;
Appearance
70 ºC PVC insulation material should be made into uniformly sized particles with a particle size of 4mm × 4mm × 3mm, or ф 4× (2-4) mm. Good plasticization, uniform color, and no obvious impurities.
Color
The color is determined through negotiation between the supply and demand parties.
Technical Analysis
Physical Property
| No. | Inspection items | Standard request | Test method | Typical value | |
| Technical Index | |||||
| 1 | Density g/cm3 | / | GB 1033 | 1.45 | |
| 2 | Tensile strength MPa | ≥16.0 | GB 1040 | 18 | |
| 3 | Elongation at Break % | ≥150 | GB 1040 | 230 | |
| 4 | Hot deformation rate (90ºC×4h) % | ≤40 | GB8815 | 20 | |
| 5 | Brittle temperature Test temperature-25ºC | Failed No.≤15/30 | GB5470 | Pass | |
| 6 | 200 ºC static thermal stability min | ≥60 | GB8815 | 70 | |
| 7 | Volume Resistivity at 20ºC Ω .m | ≥1× 1012 | GB/T 1410 | 3.2 × 1012 | |
| 8 | Dielectric Strength MV/m | ≥20 | GB/T1408. 1 | 23 | |
9 | Thermal aging property | 100±2ºC , 168h | |||
| Tensile strength MPa | ≥16.0 | GB1040 | Pass | ||
| Max Variation on Tensile Strength % | ±20 | ||||
| Elongation at break % | ≥150 | ||||
| Max Variation on Elongation at break % | ±20 | ||||
| 10 | Thermal aging quality loss | ºC | 100±2 | GB/T2951 | |
| h | 168 | ||||
| Quality loss g/m2 | ≤20 | 15 | |||
| Quality of Appearance | |||||
| 1 | Appearance | Extruded lines are smooth | Eye survey | ||
2 | Color | Consistent color tone | Eye survey | ||
| Standard deviation ≤1.5 | Colorimeter | ||||
| *Note: 1 The extruded lines are smooth, and no more than 3 floating points with a diameter ≥1.0mm are allowed within 1 meter.No particles ≥ 3.0mm are allowed. 2 All products shall undergo initial inspection upon startup, including appearance, color, density, etc. 3 If the first sample test fails, a retest is required, and the result of the second test is the judgment standard. | |||||
Using a general extruder for processing, L/D≥20
Adjust appropriately according to the equipment and extrusion status.
The following temperature profile of extruder is recommended:
| Zone | Zone 1 | Zone 2 | Zone 3 | Zone 4 | Zone 5 | Head | Die |
| TemperatureºC | 120 | 130 | 135 | 145 | 155 | 160 | 160 |
Storage and transport
It should be packaged in moisture-proof packaging, with polyethylene film bags for the inner bag and kraft paper composite bags for the outer bag, with a net weight of (25.0 ± 0.2) kg per bag. Other packaging methods agreed upon by both the seller and the purchaser are allowed.
During the transportation of the product, it should not be damaged by abnormal conditions such as sun, rain, and immersion in water. It should be kept clean, dry, not contaminated, and the packaging should be kept intact.
The product should be stored in a clean, cool, dry, and ventilated warehouse, and the storage period should not exceed six months from the date of production.
What We Have In The Field Of Telecom Optical & Electric Cable :1>Mature and Efficient Supply Chain System And Rich Industrial Resources
2>Complete Materials Demand Solutions For Cable Manufacturing And Technical Services
3>Overall Solutions And Customized Services In Factory Design, Equipment Configuration, Product Development And Rawmaterial Supply
*Quotation Varies According To Customer's Requirements And Quantity Of Produ