O7
Alloy Steel Bar
ASTM
Ferrous Steel Scrap
Hot Rolled, Forged
Round, Square, Flat
Black, Grinded, Peeled, Polished, Rough Turned
Mold Steel
Tool Steel Bar
DIN 1.2419, Sks31, 100crw6
Diameter: 20-480mm
Black, Grinded, Peeled, Polished
Annealed, Qunched and Tempered
ASTM-A681
FUSHUN
Apply The Shipping Packing
O7
Hubei, Huangshi
7228600000
Product Description
Similar Grades:
DIN1.2419, SKS31, 105CrW6
Shape:
Round, Flat, Square.
Size Range:
Steel-making Condition:
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
Chemical Composition:
Heat Treatment:
Forging: Hot forming temperature: 1050-850oC
Soft annealing: Heat to 720-750oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 230.
Stress relieving:Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening:Harden from a temperature of 800-830oC followed by oil quenching or warm bath quenching approx. 200oC. Hardness after quenching is 63-65 HRC.
Tempering: Tempering temperature: See the data bellow.
Tempering Temperature Hardness(HRC
100oC 64
200oC 61
300oC 58
400oC 54
500oC 49
600oC 41
650oC 30.
Introduction:
O7 Cold Working Die Steel is one kinds of oil hardening cold working die steel, which consists of chromium and manganese, and has higher tungsten content than grade O1. The O7 steel has the best wear resistance among the O series steels, however, it has relatively low hardenability.
Applications:
Cutting and punching tools for sheet thickness up to 6 mm, also for paper and plastics, roll shear blades for sheet thickness up to 6 mm, small bending and drawing tools, thread cutting tools, reamers, woodworking tools, gauges and other measuring tools, small inserts and plastic moulds.
Contact Information:
FUSHUN SPECIAL STEEL CO., LTD.
Website: fushunmetal.en.made-in-china.com
DIN1.2419, SKS31, 105CrW6
Shape:
Round, Flat, Square.
Size Range:
| Diameter(mm) | Thickness (mm) | Width (mm) | Length(mm) | |
| Round | 20-480 | - | - | 2000-5800 |
| Square | 20-480 | - | - | 2000-5800 |
| flat | - | 20-50 | 80-600 | 2000-5800 |
Steel-making Condition:
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
| Packing details | In seaworthy packing, as your requirement. |
| Delivery details | within 30-50 days |
Chemical Composition:
C | Mn | P | S | Si | Cr | V | W | Mo |
| 1.10-1.30 | 0.20-1.00 | 0.030max | 0.030max | 0.10-0.60 | 0.35-0.85 | 0.15-0.40 | 1.00-2.00 | 0.30max |
Heat Treatment:
Forging: Hot forming temperature: 1050-850oC
Soft annealing: Heat to 720-750oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 230.
Stress relieving:Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening:Harden from a temperature of 800-830oC followed by oil quenching or warm bath quenching approx. 200oC. Hardness after quenching is 63-65 HRC.
Tempering: Tempering temperature: See the data bellow.
Tempering Temperature Hardness(HRC
100oC 64
200oC 61
300oC 58
400oC 54
500oC 49
600oC 41
650oC 30.
Introduction:
O7 Cold Working Die Steel is one kinds of oil hardening cold working die steel, which consists of chromium and manganese, and has higher tungsten content than grade O1. The O7 steel has the best wear resistance among the O series steels, however, it has relatively low hardenability.
Applications:
Cutting and punching tools for sheet thickness up to 6 mm, also for paper and plastics, roll shear blades for sheet thickness up to 6 mm, small bending and drawing tools, thread cutting tools, reamers, woodworking tools, gauges and other measuring tools, small inserts and plastic moulds.