China Origin 4c13 Mold Die Tool Steel for Plastic High Polishing Ymt2083

Price $6.25 Compare
Min Order 1 kg
Shipping From Jiangsu, China
Popularity 289 people viewed
Quantity
+-
 

Jiangsu Longchangxing New Material Technology Co Ltd.

VIP   Audited Supplier 1 year
Profile Certified by SGS/BV
ymt2343esr
Steel Plate
AISI, DIN, JIS, GB
C: 0.33-0.43 Si: Less Than1.0
Forged
Block
Black Primer
High-strength Steel Plate, Wear Resistant Steel, Mold Steel
Die Steel Bar
Ultrasonic Testing
Customizable
Corrosion Resistance
High Hardness
High Strength
YMT
Container or Metal Framework
China
7224909090
Product Description



YMT 2083ESR


YMT2083ESR is a medium carbon, high chromium alloy, stainless mold steel (Cr>12.5%), suitable for the production of injection molds which release corrosive gas while heated in production, or molds that require cooling water to maintain efficient cooling effect.

*Good through-hardening property  
*High hard 
*Excellent polishing effect 
*High corrosive resistance.

Chemical Composition %

Steel gradeCSiMnCrMoNi
% in weight~0.38~1.00~0.60~13.00~0.25~0.30
        
        

Main Application
Apply on injection molding with corrosive resin, such as PVC; extrusion forming thermosetting resin, manufacture of phenolic (electric wood) electrical insulation devices, and semiconductor seals, mass production of disposable tableware, fast food boxes, spoons, knives and forks (from which function as preventing cooling water rust, maintaining rapid cooling, shortening the injection cycle) need higher polishing effect and higher corrosion resistance. It is recommended to choose YMT2083ESR SUP, with the following products:

Cameras, Glasses, Magnifying glass lenses, disposable needles, cups, premium cosmetic containers, etc.




Physical Property
Density: 7.73 (g/cm3)   
Specific heat capacity: 460 (J/Kg.K) 
Thermal conductivity: 30.0(W/m.K)

Elastic modulus: (103xN/mm2)
20ºC200ºC400ºC
220205190

Linear thermal expansion coefficient: 10-6C-1
20-100OC20-200OC20-300OC20-400OC20-500OC
10.510.911.311.612.0





Non-metallic Inclusion
As per ASTM 45 method A, At≤1.5, Bt≤1.5, Ct≤1.5, Dt≤1.5; Ad≤1.5, Bd≤1.5, Cd≤1.5, Dd≤1,5 or DIN50602-K4≤20 or mutual technical agreement

UT Test Standard
As per SEP 1921 Group 3, Class E/e or by mutual agreement.

Delivery Condition
Soft annealing, with hardness maximum 241HB

Tempering and Hardness
Tempering temperature20OC100OC200OC300OC400OC500OC600OC
Hardness (HRC)56565552515242


                                                             
Heat Treatment
Annealing temperatureQuenching temperatureTempering / Aging Temp
730-780OC980-1030OC250-570OC



Forging Temperature
Forging temperature: 1050-850OC