Product Description
ZnAl(Zinc alloy wire) is a product, it creates the optimum corrosion resistance against sodium chloride (salt), sulfur dioxide in marine environments. It is the optimal protection against salt. An ideal anti-corrosion protective coating of seawater.
Zinc-aluminium wire is the best for spraying, As corrosion protection spraying wire, which is suitable for arc and flame spraying processes, was used as a coating sprayed onto the steel. Specially suitable for zinc patching of welding seam in tube welding line. and capacitor spray.
The alloy produces a coating with the best anti-corrosion characteristics of both metals for optimum corrosion protection along with many uses as a solder wire.
Product code:ZA
Chemical composition:
Mechanical characteristics:
Diameter: 1.0mm≤Ф≤4.76mm
Product packing:
Pallet will be used, such as 1100mmX1100mm, 1200mmX800mm, 1000mmX1000mm, 800mmX800mm. 
Thermal spraying with Zinc-aluminium alloy wire Zn85Al15 can be easily applied to a properly blasted surface up to a 0,5 mm thickness in just one application. The coating is dry on contact allowing sealers and/or topcoats to be applied immediately when specified. One application can last over 15 years without the need for maintenance. Long-lasting protection of the surface.
We are looking forward to your cooperation!
Zinc-aluminium wire is the best for spraying, As corrosion protection spraying wire, which is suitable for arc and flame spraying processes, was used as a coating sprayed onto the steel. Specially suitable for zinc patching of welding seam in tube welding line. and capacitor spray.
The alloy produces a coating with the best anti-corrosion characteristics of both metals for optimum corrosion protection along with many uses as a solder wire.
Product code:ZA
Chemical composition:
| Item | Main elements (%) (min) | Impurities (≤)%(max) | |||||
| Zn | Al | Fe | Pb | Cd | Cu | ∑ | |
| ZA2 | REMAINING | 1-3 | 0.05 | 0.005 | 0.002 | 0.01 | 0.1 |
| ZA5 | REMAINING | 4-6 | |||||
| ZA9 | REMAINING | 8-10 | |||||
| ZA15 | REMAINING | 14-16 | |||||
| ZA22 | REMAINING | 21-23 | |||||
| ZA27 | REMAINING | 26-28 | |||||
Mechanical characteristics:
| Item | Form | Tensile Strength Rm (N/mm2) | Elongation After Fracture A 100mm(%) | Specific Gravity (g/cm3) | Melting Range (ºC) | Volume Resistivity (mΩ·mm2/m) 20ºC |
| ZA2 | COLD-DRAW(Y) | ≥ 100 | ≥ 30 | 6.88-7.02 | 382-415 | ≤ 62 |
| ZA5 | COLD-DRAW(Y) | ≥ 100 | ≥ 30 | 6.5-6.7 | 382 | ≤ 60 |
| ZA9 | COLD-DRAW(Y) | ≥ 100 | ≥ 30 | 6.1-6.3 | 382-420 | ≤ 58 |
| ZA15 | COLD-DRAW(Y) | ≥ 100 | ≥ 30 | 5.6-5.8 | 382-455 | ≤ 56 |
| ZA15 | ANNEAL(O) | ≥ 200 | ≥ 30 | 5.6-5.8 | 382-455 | ≤ 56 |
| ZA22 | COLD-DRAW(Y) | ≥ 100 | ≥ 30 | 5.2-5.4 | 382-500 | ≤ 54 |
| ZA27 | COLD-DRAW(Y) | ≥ 100 | ≥ 30 | 5.0-5.2 | 382-515 | ≤ 52 |
Diameter: 1.0mm≤Ф≤4.76mm
| DIAMETER | PERMISSIBLE |
| (MM) | VARIATION |
| 1.0≤Ф≤1.65 | +0.00,-0.03 |
| 1.65<Ф≤2.00 | +0.00,-0.04 |
| 2.00<Ф≤2.30 | +0.00,-0.05 |
| 2.30<Ф≤3.20 | +0.00,-0.06 |
| 3.20<Ф≤4.76 | +0.00,-0.07 |
Product packing:
| Hard paper drum | 100-230 kg | outer diameter 550 mm, inner diameter300mm, variable height |
| Hard paper drum | 20-50 kg | outer diameter 400 mm, inner diameter190mm. variable height |
| Plastic spool | 15 kg | flange270mm, width103mm, center hole:55mm |
| Steel drum | 250 kg | outer diameter 560 mm, inner diameter310mm, height 800mm |
| bundle | 20-25 kg |
Thermal spraying with Zinc-aluminium alloy wire Zn85Al15 can be easily applied to a properly blasted surface up to a 0,5 mm thickness in just one application. The coating is dry on contact allowing sealers and/or topcoats to be applied immediately when specified. One application can last over 15 years without the need for maintenance. Long-lasting protection of the surface.