Audited Supplier
| Product Parameters: Stainless Steel rod | |
| Material | 410 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Global Leader in Stainless Rod and Round Bar Fabrication Services
ASTM A479 AISI 410 Stainless Steel Round Bar, ASTM A479 SS 410 Square Bar, 410 Stainless Steel Flat Bar, 410 Stainless Steel Rod, Extensive Range of Stainless Steel 410 Round Bar, SS 410 Round Bar, SS DIN 1.4006 Round Bar Manufacturers, Buy Stainless Steel 410 Bright Bar, 410 SS Polished Bar, SS 410 Rod Suppliers, China AISI SS 410 Round Bar Producers.
Our stainless steel rods and bars are meticulously heated and rolled through multiple passes in a rolling mill. They offer a complete range of specifications and their performance consistently meets all industry standards and requirements.
Cold Drawn Bright Stainless Steel Rods
Cold-drawn stainless steel rods are produced under cold working conditions, resulting in a smooth surface that can be further polished and ground for enhanced finish.
Forged Stainless Steel Rod and Bar
Forged stainless steel rods undergo multiple forging processes to significantly enhance their mechanical properties and strength, ensuring superior performance.
Our extensive service centers network stocks a vast array of stainless steel bar products, ensuring a fast and ready supply of common bar sizes and alloys. We produce custom-sized stainless steel bars and offer stocking programs for orders below factory minimums to ensure prompt and fast turnaround. Daxun Alloys stocks stainless steel round bars ranging from 1/16" to 26" in diameter, available in nearly every grade, including 302, 303, 304/L, 309/S, 310/S, 316/L, 317/L, 321, 321/H, 347, 347H, 410, 416, 420, 440C, 17-4PH, Duplex 2205, and Alloy 20.
Our unique processed bar grade inventory includes stainless steel round bars, melted to consistent standards for improved machinability and reduced total part costs. With advanced bar processing machinery, Daxun Alloys can manufacture products to the precise specifications of our customers.
1. Heat Treatments: Daxun can perform specialized heat treatments on our stainless steel bars based on the metal's chemistry. 2. Positive Material Identification (PMI): In certain cases, additional PMI testing may be required, which we can complete in-house or through an independent laboratory. 3. Ultrasonic Testing (UT): This utilizes high-frequency sound energy for defect detection/evaluation, dimensional measurement, and more to ensure our stainless steel bar products meet the highest standards.
For more information on stainless steel rods, please contact Daxun.
410 Stainless Steel Rod Chemical Composition
| UNS No | S41000 |
| EN | 1.4006 |
| AISI | 410 |
| Carbon (C) | 0.08/0.15 |
| Silicon (Si) | 1 |
| Manganese (Mn) | 1 |
| Phosphorus (P) | 0.04 |
| *** (S) | 0.03 |
| Chromium (Cr) | 11.5/13.5 |
| Molybdenum (Mo) | |
| Nickel (Ni) | 0.75 |
| Property | Value |
| Density | 7.8 g/cc |
| Yield Strength | 1,225 MPa at a strain of 0.2% |
| Ultimate Tensile Strength | 1,525 MPa |
| Hardness | 126-192 Brinell hardness (annealed condition) 201-255 Brinell hardness (when hardened and tempered) |
| Bulk Modulus | 200 GPa |
| Melting Point | 1,480-1,530 °C |
| Corrosion Resistance | Good corrosion resistance in mild atmospheric environments, water, and some mild chemical environments. It shows pitting corrosion and brown staining in salt water conditions and offers lower resistance to acidic environments than the austenitic stainless steel alternatives. |
| Magnetism | Permeability 700-1,000. Highly responsive to magnetic fields, act as a strong magnetic flux carrier due to its martensitic structure. |
410 Stainless Steel Rod Physical Properties
| Density (lb./ in^2) @ RT | 0.28 | |
| Modulus of Elasticity in Tension (psi x 10^6) | 29 | |
| Specific Heat (BTU/o F/lb.) | 32 to 212 oF | 0.11 |
| Thermal Conductivity (BTU/hr/ft^2/ft) | 212oF | 14.4 |
| 932oF | 16.6 | |
| Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F) | 32 to 212oF | 5.5 |
| 32 to 1,200oF | 6.5 | |
| Electrical Resistivity (micro ohms - cm) | at 70oF | 22.5 |
Daxun's Stainless Steel Rods Manufacturing Capabilities
Our forming capabilities boast state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, rolling mills for manufacturing titanium rods, along with a unique hydroforming process for part manufacturing.
Daxun's Heat Treatment Furnace
Our advanced heat treatment furnace equipment ensures the stability and high performance of our stainless steel rod materials.
Daxun's Smelting Ability
Utilizing the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace, Daxun Stainless Steel significantly reduces impurities during the smelting process, thus enhancing the performance of our finished stainless steel rods.
Our stainless steel products boast full certification and traceability, ensuring top-tier quality. We proudly supply to the foremost industries, including aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 | Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
- GENERAL PROPERTIES
Standard Martensitic Stainless Steel Bar 410 is an exceptional material, perfect for parts that endure severe stresses. It offers superior corrosion resistance coupled with impressive strength and hardness. With a chromium content of at least 11.5%, Alloy 410 round bar stands resilient against steam, moderate chemical conditions, and mild atmospheres. This versatile grade is typically delivered in a hardened yet machinable state, ideal for applications requiring high strength and moderate heat and corrosion resistance. The bar achieves optimal corrosion resistance when polished, tempered, and hardened. Specifications: UNS S41000
APPLICATIONS:
- Cutlery
- Steam and gas turbine blades
- Kitchen utensils
- Bolts, nuts, screws
- Pump and valve parts and shafts
- Mine ladder rungs
- Dental and surgical instruments
- Nozzles
- Hardened steel balls and seats for oil well pumps
CORROSION RESISTANCE:
- This alloy demonstrates outstanding corrosion resistance to air, mildly corrosive conditions, and drinking water. Proper cleaning after use ensures its durability in daily activities like sports and food preparation. It is highly resistant to low concentrations of moderate organic and mineral acids, maintaining its integrity without corroding.
Features:
- This material is magnetic in both its annealed and hardened states.
- It develops a wide range of properties when subjected to various heating methods.
- Exhibits excellent corrosion resistance to acids such as sulfuric acid.
Available Stock Sizes:
Explore specific product pages for unique sizes, and feel free to contact us for a quote on any custom size order.
SS 410 grade stainless steel round bars
410 Stainless steel round bars are remarkably versatile, finding applications in various industries from construction to automotive parts. To cater to this wide range of uses, Jiangsu Daxun Alloy Co., Ltd. offers stainless steel round bars in multiple grades and sizes. Our advanced cutting service ensures precise compliance with your requirements every time.
Can you provide Stainless Steel (SS) grinding bars and rods?
Yes, we specialize in SS grinding bars and rods with precise dimensions, exceptional roundness, and straightness, superior to standard polished bars. However, please note that the processing costs are higher.
Q1: What range of products can you supply?
A: We offer a comprehensive range of general steel types, including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L 300 series.
Additionally, we provide 400 series and duplex stainless steels like 2205, 2304, 2101, 2507, as well as high-nickel alloys such as 904L, 800H, and 600H.
Q2. Can you manufacture products based on my drawings?
Absolutely, we can create products according to your drawings to ensure they meet your exact specifications.
Q3. How does your factory handle quality control?
Quality is our top priority. We place significant emphasis on quality control throughout the entire production process, from start to finish.
Q4. Can I request changes in packaging and transportation?
Yes, we can modify the packaging and transportation methods based on your requirements,
though you will need to cover the additional costs incurred during this period.
Q5. How does your factory handle quality control?
Maintaining high quality is our priority. We consistently focus on quality control from the beginning to the end of the production process.
Q6. What is your standard delivery time?
A: Our standard delivery time is 7 to 20 working days after payment confirmation. If your order is urgent, we will expedite the production process.
Q7. What are your payment terms?
A: Options include 100% T/T in advance, Western Union for small orders,
B: 30% T/T upfront with the remaining 70% before shipment,
C: 100% Irrevocable Letter of Credit (LC) at sight for large orders.
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, we can produce DDQ materials suitable for stainless steel pots, sinks, bowls, etc. Provide us with your specific usage, and we will adjust the mechanical properties to meet your needs.
Q9: How can I obtain a sample?
A: We offer FREE samples for your evaluation and testing. For small pieces, we may cover the courier cost, depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have exported our stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, South Korea, India, Pakistan, UAE, Ukraine, and more.