High purity calcium aluminate cement refractory motar 80% 90% Al2O3 white refractory cement for castable
High Alumina Refractory Cement Product Description
Refractory cement is made of high-quality bauxite and high-quality lime as raw materials, which are mixed into raw materials with appropriate components in a certain proportion. Hydraulic cementitious material. The refractoriness of refractory cement is not less than 1580 degrees Celsius. According to different compositions, it can be divided into aluminate refractory cement, low calcium aluminate refractory cement, calcium magnesium aluminate cement and dolomite refractory cement.
Refractory cement refers to cement with a refractoriness of not less than 1580°C. Refractory cement uses bauxite and limestone as raw materials, and is a hydraulic cementitious material obtained by calcining clinker with calcium aluminate as the main component and alumina content of about 50%. According to different compositions, it can be divided into aluminate refractory cement, low calcium aluminate refractory cement, calcium magnesium aluminate cement and dolomite refractory cement. Refractory cement can be used to cement various refractory aggregates (such as corundum, calcined bauxite, etc.) to make refractory mortar or concrete, and be used for cement rotary kilns and other industrial kilns as linings.
High Alumina Refractory Cement Features
High refractoriness, High refractoriness under load
High density, low porosity
Good slag resistance and corrosion resistance
High strength and wear resistance
Good resistance to flake performance
Good thermal shock stability
Scouring resistance
Good hot strength.
Application of High Alumina Refractory Cement
High alumina cement is mainly used to configure refractory castable such as high alumina low cement castable which can build or repair furnace or kiln for heat insulation or high temperature erosion.
Technical Data of High Alumina Refractory Cement
| Product | CA-65 | CA-68 | CA-70 | CA-75 | CA-80 | |
| Chemical Composition (%) | Al2O3 | 64-66 | 67-69 | 69-71 | 73-75 | 77-80 |
| CaO | 32-34 | 29-31 | 27-29 | 23-25 | 18-20 | |
| SiO2 | 1.8 | 1.2 | 0.3 | 0.3 | 0.3 | |
| Fe2O3 | 0.6 | 0.6 | 0.3 | 0.3 | 0.3 | |
| Specific Surface (cm2/g) | 4500 | 4500 | 5000 | 5500 | 7000 | |
| Setting time (h:min) | Initial setting (min) | 0:40 | 0:40 | 0:40 | 0:45 | 0:45 |
| Final Setting (min) | 8:00 | 8:00 | 10:00 | 10:00 | 10:00 | |
| Cold Modulus of Rupture (MPa) | 24 hour | 6.0min | 6.0min | 6.0min | 6.0min | 5.0min |
| 72 hour | 8.0min | 8.0min | 8.0min | 8.0min | 6.0min | |
| Cold Crushing Strength (Mpa) | 24hour | 45.0min | 45.0min | 45.0min | 45.0min | 35.0min |
| 72hour | 70.0min | 70.0min | 70.0min | 70.0min | 60.0min | |
| Refractoriness (°C) | 1680 | 1710 | 1730 | 1750 | 1770 | |
Application of High Alumina Refractory Cement
High alumina cement is mainly used to configure refractory castable such as high alumina low cement castable which can build or repair furnace or kiln for heat insulation or high temperature erosion.
Q1. Are you Manufacturer?
A: Yes, of course, our factory is in Xinmi,zhengzhou city,Henan province.
Q2. Can we visit your company?
A: Sure,welcome at any time,seeing is believing.
Q3. Do you accept OEM?
A: Yes, we can do OEM.
Q4. What's the MOQ of trial order?
A: No limit,We can offer the best suggestions and solutions according to your condition.
Q5. What are the payment terms?
A: Usually T/T,but L/C,Western Union etc are available for us.
Q6. How long is delivery time?
A: The delivery time will be determined according to the quantity of the order.
Q7. How are your products' quality?
A: The products will be strictly inspected before shipment, so the quality could be guaranteed.
Q8. How to solve the quality problems?
A: If the products are not confirmed to customer samples or have quality problems,our company will be responsible to make compensation for it.
Q9.How about your company's certification?
A: ISO9001 and Test Report,also we could apply other necessary certification.