Audited Supplier
PC-306
Powder, White Powder
water-reducing admixture
Uhpc Powder PCE
98%
Specilized for Uhpc
Concrete Solutions
HUAXUAN
25kg/Bag
98% solid content
Shangdong/Hubei China
3824401000
Product Description
Founded in 2006,Huaxuan High-tech® is a manufacturer specializing in concrete admixtures and mortar additives. Joining forces with the scientific research teams of China's top universities and cooperating with national key engineering projects,we provide customers around the world with product terminal application technical guidance and production after-sales services in the fields of concrete, mortar, cement prefabricated products, waterproofing, refractory, coal mines, oil fields and other materials. More than 40 product series have been formed, including concrete admixtures used to systematically improve the performance of concrete, special mortars used in railway and highway projects, and mortar additives used in civil construction materials, covering:Polycarboxylate water-reducing admixtures liquid,Polycarboxylate water reducing agent powder, gypsum retarder, defoaming agent, oil field additives and functional chemical building material additives and other categories have cultivated many dealers for Southeast Asia, Middle East, Africa, Europe, United States and other regions, and provide high-quality products to global customers with excellent services.
Product Description:
PC-306 has been primarily developed for applications in the UHPC and other high strength concrete industries where the highest water reducing ratio and excellant early strength and enhanced strength performance and highest density required.
PC-306 is free from chlorides and complies with ASTM C494 Type A and F.
Conventional superplasticisers, such as those based on sulpunated melamine and naphthalene formaldehyde condensates, at the time of mixing, become absorbed onto the surface of the cement particles. This absorption takes place at a very early stage in the hydration process. The sulphonic groups of the polymer chains increase the navigate charge on the surface occurs by electrostatic repulsion.
PC-306 is differentiated from conventional superplasticisers in that it is based on a unique Polycarboxylic ether polymer with long lateral chains. This greatly improves cement dispersion. At the start of the mixing process the same electrostatic dispersion
occurs as described previously but the presence of the lateral chains, linked to the polymer backbone, generate a steric hindrance which stabilises the cement particles capacity to separate and disperse. This mechanism provides flowable concrete with greatly reduced water demand.
PC-306 production reaction temperature is fixed and can be controlled. It is not like other similar PCE,whose production temperature fluctuates in high range.
PC-306 production reaction temperature is fixed and can be controlled. It is not like other similar PCE,whose production temperature fluctuates in high range.
| Huaxuan High-tech® PC-306 Main Specifications | ||||
| No | Test Item | Criterion | Detection result | |
| 1 | Appearance and color | White or light yellow powder | White powder | |
| 2 | Solid content (%) | ≥95 | 98 | |
| 3 | Moisture content /% | ≤5.0 | 1.6 | |
| 4 | Water reduction rate /% | ≥25 | 32 | |
| 5 | Slurry fluidity (mm) | ≥220 | 240 | |
| 6 | Compressive strength ratio (%) | 1d | ≥170 | 179 |
| 3d | ≥160 | 171 | ||
| 7d | ≥150 | 154 | ||
| 28d | ≥140 | 142 | ||
| 7 | Fineness (0.3mm standard sieve residue)/% | ≤15 | 5.0 | |
| 8 | Packing density /(g/cm3) | 0.70±0.10 | 0.66 | |
| 9 | PH value (10% aqueous solution, 20ºC) | 6.0~8.0 | 6.5 | |
| 10 | Reinforcement corrosion | The presence of corrosion hazards should be indicated | No | |