| Ti 6Al-4V Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Standard | ASTM B265,AMS 4902,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS EN 10258 (formerly DIN 59381),EN 10151 ,EN 10088 EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
| Length | 1000mm-13000mm or as required |
| Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| Thickness | 0.3 to 120mm or as required |
| Technical | Hot rolled/ Cold Rolled/forging |
| surface | No.1,2D, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), hairline, brush,mirror,Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), |
| Material Grade | ASTM B265 Titanium Alloy Gr 5,Ti-6Al-4V UNS R56400 JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| sheet Sizes | 1000 x 2000 mm, 1220 x 2440 mm, 1500 x 3000 mm, 2000 x 2000 mm, 2000 x 4000 mm |
| thickness:Cold rolled 0.5-6.4 mm | |
| thickness:Hot rolled 3.0-60.0 mm | |
| Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard |
| Foil sizes | Thickness : 8-100 microns (0.00031-0.004 in) |
| Width: Up to 500 mm (19.5 in) | |
| Weight (in rolls) : Up to 50 kg (110 lb); e.g. approxi- mately 1400 m at 8 microns and ap- proximately 112 m at 100 microns. | |
| Cutting | To provide a comprehensive service, we use a variety of cutting methods, including: |
| Laser Plate Cutting,Plasma Plate Cutting,Oxy-propane Flame Cutting | |
| Plasma profiles | As per customer's drawings |
| Value added services | Laser cutting, Waterjet cutting, Plasma cutting, Bending and mechanical processing, edge preparation, welding, sawing and shearing. |
| Packing | Bundles with waterproof cloth outside or plywood box |
| Why buy UNS R56400 Sheet from DAXUN? | Free quote,Free sample,EN 10204 3.1,Mill Test Certificate is supplied with shipment.,NABL Approved Lab Reports,Any third party inspection is accepted.,Tested to ASTM A923 Method "C" or ASTM G48 Method "A".Minimum Nitrogen content and Ferrite Count Test |
DAXUN stands as a premier Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate Manufacturer and Supplier from China! Our ambition is to lead the world in producing high-performance titanium alloy plates. Delivering swiftly across the globe, we specialize in ASTM B265 Grade 2, Grade 5 Titanium Plates. At DAXUN, we manufacture and maintain a robust inventory of Grade 5 alloy titanium plates (UNS R56400) with thicknesses ranging from 0.5mm to 300mm. The 0.5mm-6.0mm range is cold rolled, 6.0-50mm is hot rolled, and anything above 50mm is expertly forged. Grade 5 titanium plate (Ti-6Al-4V) is renowned as the 'workhorse' of titanium alloys, offering a perfect blend of high strength, ductility, and superior resistance to corrosion and high temperatures, making it a top choice in both general and military industries. Our plates comply with a multitude of standards: ASTE, ASME, AMS, GB, GJB, MIL, JIS, EN, and more.
Ti-6Al-4V Grade 5 titanium plate is composed of 90% titanium, 6% aluminum, and 4% vanadium, forming an α-β titanium alloy where aluminum stabilizes the α phase and vanadium stabilizes the β phase. This alloy's key features boast superb comprehensive and process performance, including outstanding strength at both room and elevated temperatures, excellent creep resistance, thermal stability, high fatigue performance, and resistance to *** growth in seawater. Furthermore, it demonstrates satisfactory fracture toughness and hot salt stress corrosion performance. Ti-6Al-4V titanium plate is also highly processable and superplastic, making it ideal for various processing methods, welding, and machining.
The Ti-6Al-4V Grade 5 titanium plate finds its primary applications in aerospace, military sectors, power generation, vehicle armor, precision rocket guidance, and the marine industry.
Distinguished Attributes
Grade 5 titanium alloy plate is the most commercially versatile of all titanium alloys, merging high strength and toughness. Ti-6Al-4V Grade 5 titanium alloy exhibits an impressive array of properties:
- Exceptional strength
- Remarkable creep resistance
- Superior fatigue resistance
- Heat treatable for enhanced performance
- Notable ductility
- Outstanding plasticity
- Excellent weldability
- Operational range from -196°C to 450°C
Typical Applications
Ti-6AL-4V titanium plates and sheets serve crucial roles in components requiring corrosion and stress corrosion resistance, combined with high strength (400-450°C) and good ductility. These applications include: 1. Jet engine compressor blades, disks, rings, and fuselage components like wings, turbine disks, doors, bulkheads, as well as military aircraft hardware heat shields, engine nozzles, landing gear doors, and superplastic forming parts. 2. Military uses span armor, guidance systems, shell casings, and more. 3. Spacecraft components, including ***s and heat shields. 4. Medical and surgical instruments. 5. Sports equipment, such as bicycle frames and golf clubs. 6. Other applications requiring a high strength-to-weight ratio.
Quality Assurance, Prompt Delivery, Rigorous Inspection
Daxun implements thorough quality assurance tests, encompassing flattening tests, pitting and resistance tests, mechanical tests, hardness tests, material positive identification, and expansion tests. These tests affirm the material's suitability for its intended applications. Throughout production, we meticulously measure the product's diameter, thickness, and surface. Our standard delivery timeframe is 5-7 days, extending to 15-20 days for special size products.
- We adhere strictly to contract stipulations for delivery times.
- We welcome third-party agency inspections at our factory.
- Free samples are available for customer testing.
- We support on-site or video factory inspections to ensure transparency and confidence.
Discover the unparalleled chemical composition of our (Ti 6AL-4V) Grade 5 Titanium Sheet, a pinnacle of advanced metallurgy.
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
Uncover the meticulous chemical composition of Grade 2 Titanium.Sheet, designed for robust yet adaptable performance.
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
Explore the mechanical properties of Grade 2 Titanium, crafted for diverse industrial needs. Sheet, delivering consistency and durability for every project.
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
DAXUN is your titanium authority, specializing in a wide range of titanium plate projects, from the smallest to the most mammoth. As your reliable reference point and enduring partner, DAXUN stands ready to offer unparalleled titanium plates and comprehensive technical support tailored to your business needs. With DAXUN, you're not just engaging a supplier of premium industrial pure titanium plates and robust titanium alloy plates; you're aligning with a strategic ally dedicated to overcoming any challenge and fulfilling your project aspirations with precision and dedication.
At DAXUN's state-of-the-art service center in China, we maintain a dynamic inventory of titanium plate products to ensure swift order processing. Our value-added services, including basic processing, precision water jet cutting, and meticulous plate nesting, empower our customers by significantly reducing time and costs.
DAXUN's relentless investment in cutting-edge production facilities, coupled with strategic capacity agreements with our partners, cements our position at the pinnacle of titanium plate quality, both now and in the future.
Reach out to DAXUN today for the most competitive titanium plate prices and up-to-date technical insights.
A global leader in high performance Ti-6Al-4V titanium plate alloy grade5 titanium plate manufacturing services
Grade 5DAXUN is a Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate Manufacturer and Supplier from China! With the goal of creating the world's high-performance titanium alloy plates. We deliver quickly worldwide - ASTM B265 Grade 2, Grade 5 Titanium Plates. DAXUN produces and stocks alloy titanium plates Grade 5 (UNS R56400) with thicknesses ranging from 0.5mm to 300mm (0.5mm-6.0mm is cold rolled. 6.0-50mm is hot rolled, and 50mm and above are forged). Grade 5 titanium plate (Ti-6Al-4V) is the "workhorse" of titanium alloy materials. It combines high strength, ductility and excellent corrosion resistance, high temperature resistance, thus being favored by many general and military industries. Compliant with: ASTE, ASME, AMS, GB, GJB, MIL, JIS, EN, etc.
Ti-6Al-4V grade 5 titanium plate is mainly used in aerospace, military industry, power industry, vehicle armor, rocket precision guidance parts, marine industry, etc.
Grade 1
Today, DAXUN Alloys is a leading global producer and supplier of high-quality Grade 1 titanium plate.
Pure Grade 1 titanium plate has excellent ductility and cold formability, making it ideal for deep drawing. Grade 1 titanium is known for its excellent general and seawater corrosion resistance, as well as its resistance to oxidizing, neutral and mildly reducing media (solutions), including chlorides. Titanium's low density (about half that of nickel-based alloys), high strength-to-weight ratio and corrosion resistance make it an excellent choice for a wide range of harsh chemical conditions. Commercially pure Grade 1 titanium is the softest and most ductile. It has good cold formability and excellent corrosion resistance. It also has excellent weldability and good impact hardness.
ASTM B265 Titanium Gr 1 Plate Producers, Titanium Gr 1 Sheets, Titanium Gr 1 Finished Plates, ASTM B265 Titanium Grade 1 Coil Suppliers, Pure Titanium Titanium Gr 1 Hot Rolled Plates, Titanium Gr 1 Cold Rolled Plates, Titanium ASTM B265 Gr 1 Sheets, Gr 1 Titanium Patterned Plates Dealers, Titanium Gr 1 Perforated Plates, Titanium Grade 1 Sheets and Plates Manufacturers in China.
Grade2
DAXUN produces and stocks commercially pure titanium plates Grade 2 (UNS R50400) in thicknesses ranging from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the "workhorse" of the commercially pure titanium family. It combines high strength, ductility, and excellent corrosion resistance for many industrial applications.
Grade 2 Titanium Plate is a commercially pure titanium plate. It offers an excellent balance between strength and ductility. It has good impact strength and is easily weldable. It has good corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. It also has excellent resistance to seawater and salt solutions.
Titanium's low density, high strength-to-weight ratio, and corrosion resistance make it an ideal material for a wide range of applications, and it effectively resists stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a melting point of 1660°C, Grade 2 Titanium Plate is the alloy of choice for most industrial applications requiring good ductility and corrosion resistance.
DAXUN is a metal expert focused on small and large titanium plate projects. DAXUN is your reference point and long-term partner, ready to provide you and your business with titanium plates and any technical assistance you may need. You can consider DAXUN not only as your supplier of industrial pure titanium plates and titanium alloy plates, but also as your strategic partner to help you meet any challenges and needs you may encounter, ultimately allowing you to achieve your project goals.
At DAXUN's premier service center in China, we boast an extensive stock of titanium plate products, ensuring swift order processing. With our advanced capabilities in basic processing, precision water jet cutting, and efficient plate nesting, we enhance value for our customers by significantly reducing both time and costs.
Our unwavering commitment to continuous investment in DAXUN's state-of-the-art production facilities, alongside strategic capacity agreements with our esteemed partners, ensures that DAXUN remains a leader in titanium plate quality, both today and in the future.
Reach out to DAXUN today to access the most competitive titanium plate prices and receive comprehensive technical information tailored to your needs.