HH-H10Mn2
Rolling Wire
Stainless Steel
Not Containing Flux
Acidic
>20mm
Accepted
Negotiable; Around 30-35 Days
ISO 9001; CE; RoHS; Reach; OHSAS
200000 Tons
Honglu
0.8; 1.0; 1.2; 1.6
Anhui, China
7505220000
Product Description
| sports event | tensile strength Rm/MPa | yield strength ReL/Rp0.2MPa | elongation A% |
| standard value | 490-670 | >=490 | >=18 |
| example value | 564 | 459 | 29 |
Versatile Uses: Ideal for the automatic submerged arc welding of both carbon and low alloy steel, matching the same strength level. Perfectly suited for applications in the construction of ships, petrochemical plants, and boilers, among others.
Distinguishing Characteristics: HH-H10Mn2 is a premium copper-plated, non-alloy submerged arc welding wire, paired with SJ101 flux that ensures exceptional welding process performance. It creates beautifully shaped weld channels, is easy to deslag, and delivers impressive low-temperature impact toughness.
Chemical Composition of Welding Wire: Composition (Mass Fraction) 100%
| sports event | C | Mn | Si | S | P | Cr | Ni | Cu |
| standard value | <=0.12 | 1.50-1.90 | <=0.07 | <=0.030 | <=0.030 | <=0.20 | <=0.30 | <=0.35 |
| example value | 0.11 | 1.65 | 0.05 | 0.017 | 0.022 | 0.022 | 0.02 | 0.116 |
1. Ensure the flux is properly baked at a temperature range of 250-400 ºC for 1-2 hours. The welding wire should be kept dry and free from oil and rust before use.
2. Prior to welding, clean the surface to remove any rust, oil, water, and other impurities.
3. Maintain sulfur content of the flux at <= 0.050% and phosphorus content at <= 0.060% to ensure quality.