FMA
1770< Refractoriness< 2000
Block
60%Min.
White
3.3G/Cm3
1500-1800degree
Long Time Materials
Refractory Material
Bauxite, Magnesia
YZSD
Bag
GB
China
Product Description

magnesia , alumina ,aluminium , aluminum ,magnesite
Choosing best quality a-Al2O3 powder and high purity burn magnesia powder as raw material ,
sintered after 2200celsius degree in electric arc furnace.
Fused magnesia-alumina spinel have following features:
1.big bulk density
2.Good thermal shock resistant
3.Good anti-erosion property
Main application:
a.For high quality refractory castable
b.As material for slide gate and lining brick of ladle etc.
Item | MA-70 Grit Powder >0.1mm ≤0.1mm | MA-65 Grit Powder >0.1mm ≤0.1mm | |||||||
Chemical composition | Al2O3% ≥ | 67-75 | 67-75 | 64-68 | 64-68 | ||||
SiO2% ≤ | 0.4 | 0.4 | 0.6 | 0.6 | |||||
Fe2O3% ≤ | 0.5 | 0.5 | 0.25 | 0.3 | |||||
MgO%≤ | 23-31 | 23-31 | 31-35 | 3135 | |||||
Physical property | Magnetic conternt % ≤ | 0.05 | 0.1 | 0.05 | 0.1 | ||||
Apparent porosity%≤ | 5.0 | 3.0 | |||||||
Bulk density g/cm3≥ | 3.30 | 3.30 |