Audited Supplier
alloy steel bar
Round
AISI, ASTM, DIN, JIS
Ferrous Steel Scrap
Forged
Bar
Rough Maching or Black Surface
Shaft
Structural Steel Bar
Hot Forging
Black or Bright
Alloy Steel Bar or Carbon Grade
1045 4140 4150 Scm440
dajin
Seaworthy Packaging
200-800mm
China
72285000
Product Description
Forged Alloy Steel Round Bar 4140 1.7225
Hot forging steel bar
Forged parts
SCM440 SCM435 4130 4140 4145 forged bars
1.Chemical Composition (%):
2.Available sizes:
Round: Dia. 16 - 1000mm
16mm-350mm with hot rolled supply condition;
200-1000mm with forged supply condition
3.Delivery condition: Hot rolled or forged, Peeled or black surface, annealed or QT.
4.Applications:
Statically and dynamically stressed components for vehicles, engines and machines. For parts of larger cross-sections, crankshafts, gears.
5.Heat Treatment:
Soft annealing: heat to 680-720°C, cool slowly.
Hardness after annealing: Max. 241 HB
Hardening: 820 - 850 °C
Normalizing temperature: 840-880°C
Tempering: 540-680°C
6. Inspection: 100% Ultrasonic according to the test standards:SEP1921-84,GR.3 CLASS C/C
7. Packing situation: standard seaworthy packing or as customer required
8. Delivery time: 30 days after order confirmed
9. Process: EAF+LF+VD ( necessary) +UT+ Peeled(optional) +Turned (optional) + Heat Treatment (optional)
Hot forging steel bar
Forged parts
SCM440 SCM435 4130 4140 4145 forged bars
1.Chemical Composition (%):
| Grade | C | Si | Mn | P | S | Cr | Mo |
| 42CrMo4 | 0.38-0.45 | 0.17-0.37 | 0.40-0.70 | ≤0.035 | ≤0.035 | 0.90-1.20 | 0.15-0.25 |
| 1.7225 | 0.38-0.45 | ≤0.40 | 0.60-0.90 | ≤0.025 | ≤0.035 | 0.90-1.20 | 0.15-0.30 |
| 4140 | 0.38-0.43 | 0.15-0.35 | 0.75-1.00 | ≤0.035 | ≤0.040 | 0.80-1.10 | 0.15-0.25 |
Round: Dia. 16 - 1000mm
16mm-350mm with hot rolled supply condition;
200-1000mm with forged supply condition
3.Delivery condition: Hot rolled or forged, Peeled or black surface, annealed or QT.
4.Applications:
Statically and dynamically stressed components for vehicles, engines and machines. For parts of larger cross-sections, crankshafts, gears.
5.Heat Treatment:
Soft annealing: heat to 680-720°C, cool slowly.
Hardness after annealing: Max. 241 HB
Hardening: 820 - 850 °C
Normalizing temperature: 840-880°C
Tempering: 540-680°C
6. Inspection: 100% Ultrasonic according to the test standards:SEP1921-84,GR.3 CLASS C/C
7. Packing situation: standard seaworthy packing or as customer required
8. Delivery time: 30 days after order confirmed
9. Process: EAF+LF+VD ( necessary) +UT+ Peeled(optional) +Turned (optional) + Heat Treatment (optional)